Eur. Phys. J. E (2008) 26: 43-53
https://doi.org/10.1140/epje/i2007-10341-x

ISMC-2007

NMR investigations of polymer dynamics in a partially filled porous matrix

¹ Department of Macromolecular Chemistry, RWTH Aachen University, 52074, Aachen, Germany
² Department of Technical Physics II/Polymer Physics, TU Ilmenau, PO Box 100565, 98684, Ilmenau, Germany

^* e-mail: siegfried.stapf@tu-ilmenau.de

Received: 19 September 2007
Accepted: 16 May 2008
Published online: 22 May 2008

Abstract

The interior surface of well-defined porous alumina membranes (Anopore) of 20nm and 200nm pore diameter, respectively, was coated with polymer layers generated from solution by the solvent evaporation method. Deposits of poly(dimethyl siloxane) (PDMS) with nominal thicknesses ranging from 0.15 to 4.5nm --corresponding to submonolayer to multilayer films-- were investigated, and were compared to poly(butadiene) (PB) as an example for non-wetting polymers. Molecular weights below and above the critical value were studied since the bulk dynamics of such polymers are known to be qualitatively different. First results of NMR relaxation dispersion experiments on these systems are presented, supplemented by transverse relaxation times and double-quantum measurements obtained from high-field NMR. A systematic decrease of relaxation times at low fields with decreasing polymer amount is found for PDMS, but molecules retain a high degree of mobility irrespective of molecular weight. The relaxation dispersion results are supported by T₂ data and ¹H residual dipolar coupling (RDC) constants, and are discussed in terms of molecular order and reorientational dynamics.